ASTM A790 Uns S31803 Smls Pipe X 5.7-6.3m
-
Price:
Negotiable
- minimum:
- Total supply:
-
Delivery term:
The date of payment from buyers deliver within days
-
seat:
Zhejiang
-
Validity to:
Long-term effective
-
Last update:
2017-11-29 00:46
-
Browse the number:
199
+
Huzhou Dapu Stainless Steel Co., Ltd.
- Contactaixin:
Mr. Jack Li(Mr.)
- Email: telephone: phone:
-
Arrea:
Zhejiang
Address:Jinshiji Building Room No. 1241, Huzhou, Zhejiang, China 313000
- Website:
+
We are professional manufacture of stainless steel welded pipe and seamless pipe in China.
Grade:
304(0Cr18Ni9 ) 304L(00Cr19Ni10 ) 321(1Cr18Ni9Ti )
321(0Cr18Ni10Ti)316(0Cr17Ni12Mo2)316L(00Cr17Ni14Mo2)316L (00Cr18Ni12Mo2Ti)310S(0Cr25Ni20) 310S(1Cr25Ni20Si2)904L(00Cr20Ni25Mo4)201
Size:
Diameter range: 6mm-630mm
Wall thickness: 0.5mm-60mm
Length: The max is 12m or as customers' required
Processing:
Cold drawn or cold rolled
Grade:
304(0Cr18Ni9 ) 304L(00Cr19Ni10 ) 321(1Cr18Ni9Ti )
321(0Cr18Ni10Ti)316(0Cr17Ni12Mo2)316L(00Cr17Ni14Mo2)316L (00Cr18Ni12Mo2Ti)310S(0Cr25Ni20) 310S(1Cr25Ni20Si2)904L(00Cr20Ni25Mo4)201
Size:
Diameter range: 6mm-630mm
Wall thickness: 0.5mm-60mm
Length: The max is 12m or as customers' required
Processing:
Cold drawn or cold rolled
Grade | Chemical Composition | Others | Mechanical Properties, min | |||||||||||
ASTM | Tensile Strength Ksi (Mpa) |
Yeild Point Ksi (Mpa) |
Elongation % min |
Hardness Test Max | ||||||||||
C | Si. | Mn | P | S | Ni | Cr | Mo | HB | HRB | |||||
max | max | max | max | max | min | min | min | |||||||
304 | 0.08 | 0.75 | 2.00 | 0, 045 | 0.03 | 8.00~11.00 | 18.00~20.00 | - | - | 75(515) | 30(205) | 35 | 192 | 90 |
304 L | 0.035 | 0.75 | 2.00 | 0, 045 | 0.03 | 8.00~13.00 | 18.00-20.00 | - | - | 70(485) | 25(170) | 35 | 192 | 90 |
309 | 0.15 | 0.75 | 2.00 | 0, 045 | 0.03 | 12.00~15.00 | 22.00~24.00 | - | - | 75(515) | 30(205) | 35 | 192 | 90 |
310 | 0.15 | 0.75 | 2.00 | 0, 045 | 0.03 | 19.00~22.00 | 24.00~26.00 | - | - | 75(5150 | 30(205) | 35 | 192 | 90 |
316 | 0.08 | 0.75 | 2.00 | 0, 045 | 0.03 | 11.00~14.00 | 16.00~18.00 | 2.00~3.00 | - | 75(515) | 30(205) | 35 | 192 | 90 |
316 L | 0.035 | 0.75 | 2.00 | 0, 045 | 0.03 | 10.00~15.00 | 16.00~18.00 | 2.00~3.00 | - | 70(485) | 25(170) | 35 | 192 | 90 |
316 Ti | 0.08 | 0.75 | 2.00 | 0, 045 | 0.03 | 11.00~14.00 | 16.00~18.00 | 2.00~3.00 | Ti: 5xC% ~0.75 | 75(515) | 30(205) | 35 | 192 | 90 |
317 | 0.08 | 0.75 | 2.00 | 0, 045 | 0.03 | 11.00~14.00 | 18.00~20.00 | 3.00~4.00 | - | 75(515) | 30(205) | 35 | 192 | 90 |
321 | 0.08 | 0.75 | 2.00 | 0, 045 | 0.03 | 9.00~13.00 | 17.00~20.00 | - | Ti: 5 x C% ~ 0.70 B | 75(515) | 30(205) | 35 | 192 | 90 |
321 H | 0.04~ 0.10 | 0.75 | 2.00 | 0, 045 | 0.03 | 9.00~13.00 | 17.00~20.00 | - | Ti: 4 x C% ~0.60 | 75(515) | 30(205) | 35 | 192 | 90 |
347 | 0.08 | 0.75 | 2.00 | 0, 045 | 0.03 | 9.00~13.00 | 17.00~20.00 | - | Nb + Ta: 10 x C% ~1.00 | 75(515) | 30(205) | 35 | 192 | 90 |
347 H | 0.04~ 0.10 | 0.75 | 2.00 | 0, 045 | 0.03 | 9.00~13.00 | 17.00~20.00 | - | Nb +Ta: 8 XC% ~ 1.0 | 75(515) | 30(205) | 35 | 192 | 90 |
410 | 0.15 | 1.00 | 1.00 | 0, 040 | 0.03 | 0.75 | 11.5~13.5 | - | - | 60(415) | 30(205) | 20 | 207 | 95 |
430 | 0.12 | 1.00 | 1.00 | 0, 040 | 0.03 | 0.75 | 16.00~18.00 | - | - | 60(415) | 35(240) | 20 | 190 | 90 |